Two component acrylate adhesive formula (Part 2)

[formula] Xi 5acrylate adhesive

component mass component mass component

A: Neoprene 30 methyl methacrylate 65

benzoyl peroxide 5,6-di-tert-butyl-p-methylphenol 0.15

B: n, n-xylidine 0.25

prepare and cure at room temperature for 5min

performance and application the shear strength of plastic plate is 10.8mpa. It is mainly used for bonding plexiglass, plastic plates, etc

[formula] twelve 6pacrylate adhesive

add 207 parts of ethylene glycol diglycidyl ether, 48 parts of methacrylic acid and 3.5 parts of triethylamine into the reactor, stir at 50 ℃ for 10h, then add

12 parts of acrylic acid, and continue to react at 55 ℃ for 9h to obtain a viscosity of 3pa S. The specific formula is as follows

component mass component mass component

A: mixed ester 100 methyl ethyl ketone peroxide 3

acrylic acid 40 vinyl acetate 30

B: Vinyl thiourea 0.5 cobalt oleate 0.05

cobalt naphthenate 0.03 butanone 80

preparation and curing apply the two components a and B respectively on the two test pieces. From the morphology, they will be overlapped after 30s. 24h to reach the maximum strength

performance and application the metal shear strength is 11.1mpa. The adhesive is mainly used for oil surface metal bonding

[formula] thirteen low temperature resistant structural adhesive

component mass component mass component

methyl methacrylate 628.5 methacrylic acid 50

chloroprene rubber 114 peroxide slurry 100

methyl methacrylate/butadiene/styrene glycol graft copolymer 200 N, n-dimethylp-xylidine 7.51

preparation method The amine and peroxide slurry are mixed evenly to obtain an adhesive with a tensile strength of

36.5mpa. With the help of this international platform, we have demonstrated petroleum based materials, bio based materials Nearly 100 kinds of products in additive manufacturing and other fields

[formula] Tetraterpene tackifying acrylic adhesive

component mass component mass component

butyl acrylate 85 methyl methacrylate 15

lauryl mercaptan 0.5 2-polystyrene ethyl methacrylate 10

azodiisobutyronitrile 0.01 3-methacryloyloxypropyl trimethoxysilane 0.7

terpene phenolic resin 50 dibutyltin bislaurate 0.02

preparation method lauryl mercaptan, silane derivatives and three acrylates, Free radical polymerization was carried out under the initiation of azodiisobutyl ester, and the polymer solution was prepared after 8h of reaction. The adhesive was prepared by mixing the polymer solution with terpene phenolic resin and dibutyltin compound

the usage is the same as that of general acrylic adhesive

characteristics this terpene phenolic resin tackifying acrylic adhesive has high bonding strength and high temperature adhesion, and its shear adhesion is 2lokpa

[formula] 15 millionth glue

6. Cooler: component mass component component mass component

main agent: methyl methacrylate 46 anhydrous methacrylic acid 10

chlorosulfonated polyethylene (hypolon) 40 ethylene glycol dimethacrylate 1

cumene peroxide 2

primer: nn n, N-dimethylaniline 1

method of use: apply primer on one side and main agent on the other side, The two surfaces are compacted and cured at room temperature for about 5~6min, and high strength can be achieved after 1h

[formula] sixteen SGA glue

component quality component also has policy support advantage component quality component

A: nitrile rubber 33 methyl methacrylate 34

bpo 5 hydroquinone 0.5

B: n, N-dimethylaniline 1

safety protection is toxic, with great odor and irritation

packaged, stored and transported in tubes, kept cool and dry

source: fine chemicals in the 21st century